Dry etching method

ABSTRACT

A dry etching method is disclosed, in which the pressure of etching gas in a reaction chamber, the bias voltage applied to article to be etched, and the temperature of the article to be etched object are set so that the etching rate for the article to be etched is greater than 0.2 μm/min, a ratio of the length of side etching in the article to be etched to the depth of etching therein is less than 1/100, and a ratio of the etching rate for the article to be etched to the etching rate for a mask formed thereon is greater than 10. Thus, the dry etching method can satisfy three requirements (that is, a high etching rate, a high selection ratio and marked anisotropy in etching) at the same time, although conventional dry etching methods can satisfy only two of three requirements.

This application is a Continuation of application Ser. No. 07/225,813, filed Jul. 29, 1988 now abandoned.

BACKGROUND OF THE INVENTION

The present invention relates to a dry etching method, and more particularly, to a dry etching method capable of etching an article to be etched at a high rate and in exact accordance with a mask pattern.

The improvements in etching rate, selectivity and anisotropy of dry etching are described in the Proc. Dry Process Symp., 1986, page 42, the Proc. Dry Process Symp., 1986, page 83 and the Proc. Dry Process Symp., 1984, page 121, respectively, and are further described in many other publications. A dry etching method capable of satisfying two of three requirements (a high etching rate, high selectivity and marked anisotropy) is disclosed in, for example, a Japanese Patent Application JP-A-60-158,627. Further, a low-temperature dry etching method has been proposed.

However, conventional dry etching methods cannot satisfy the above-mentioned three requirements at the same time, but satisfy only one or two of the requirements. For example, in a conventional method, the etching rate is as high as 0.5 μm/min and a ratio of the length of side etching to the etching depth is less than 1/100, but a selection ratio (that is, a ratio of the etching rate for an article to be etched to that for a mask material) is less than 5. Accordingly, the mask may be etched off in the course of an etching operation. In order to solve this problem, it is required to form a mask of an etching resistant film, for example, an SiO₂ film. In this case, a manufacturing process is very complicated. Further, in another conventional method, the etching rate for an article to be etched is greater than 0.5 μm/min and a ratio of the etching rate for the article to be etched to that for a mask material is greater than 10, but the length of side etching increases. Accordingly, a pattern formed in the article to be etched deviates from a mask pattern by 0.1 to 0.2 μm, and such a deviation makes a large scale integration circuit defective. In a further conventional method, a ratio of the length of side etching to the etching depth and a ratio of the etching rate for the article to be etched to that for a mask material are both high, but the etching rate for the article to be etched is as low as about 0.1 μm/min. Accordingly, it takes a very long time, for example, to form a deep groove in a silicon substrate by dry etching.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a dry etching method which can satisfy three requirements for dry etching (that is, a high etching rate, high selectivity and marked anisotropy) at the same time to solve the difficulties of conventional methods.

In order to attain the above object, according to the present invention, there is provided a dry etching method in which dry etching is carried out in such a manner that an etching gas which does not contain carbon and silicon and does not deposit a film on the article to be etched, is kept at a pressure higher than the pressure of etching gas used in conventional anisotropic etching, each of a bias voltage applied to the article to be etched and electric power supplied to the etching gas is put in a predetermined range, and the temperature of the article to be etched is so set as to obtain marked anisotropy in etching the article to be etched and to make an etching rate for a mask material less than one-half an etching rate for the mask material at 20° C.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph for explaining an embodiment of a dry etching method according to the present invention.

FIGS. 2 to 4 are graphs for explaining another embodiment of a dry etching method according to the present invention.

FIG. 5 is a graph for explaining a further embodiment of a dry etching method according to the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

When the pressure of etching gas in a reaction chamber of the etching apparatus is made higher than an ordinary gas pressure used in carrying out anisotropic etching, and a gas which does not contain carbon and silicon so as not to deposit a film (that is, a film containing carbon or silicon) on the article to be etched in an etching process, is used as an etching gas, ions and radicals resulting from the etching gas are not consumed for removing the deposited film, and moreover the pressure of the etching gas is high. Accordingly, the etching rate or the article to be etched is higher than an etching rate obtained in a case where a gas which contains carbon and silicon and thus produces the deposit on the article to be etched, is used as the etching gas. For example, in a case where an SF₆ gas is used as the etching gas, an etching rate for silicon is greater than 0.5 μm/min. Further, when the pressure of an etching gas is made higher than an ordinary gas pressure used in carrying out anisotropic etching and each of a bias voltage applied to the article to be etched and electric power supplied to the etching gas is put in a predetermined range shown in the following TABLE I, a ratio of the etching rate for the article to be etched to that for a mask material is greatly increased, that is, the selectivity in an etching process is greatly improved. Furthermore, when the temperature of the article to be etched is put in a predetermined range shown in the following TABLE I to make a ratio of the length of side etching to the etching depth less than 1/100 and to make at etching rate for a mask material less than one-half an etching rate for the mask material at 20° C., the anisotropy in etching is greatly improved and the selectivity in an etching process is further improved.

Etching conditions used in the present invention are summarized in the following TABLE I.

                  TABLE I                                                          ______________________________________                                                Etching method                                                                                           Magnetron                                                          Microwave   discharge                                              Reactive    plasma      type reactive                                 Item     ion etching etching     etching                                       ______________________________________                                         Gas pressure                                                                             60 to 100   4 to 10     4 to 10                                      (m Torr)                                                                       Bias voltage                                                                            -100 to -30 -50 to -10  -50 to -10                                    (V)                                                                            Electric 0.2 to 0.4  200 to 400  0.2 to 0.4                                    power    (W/cm.sup.2)                                                                               (W)         (W)                                           Temperature                                                                              -90 to -135                                                                               -100 to -135                                                                               -100 to -135                                  (°C.)                                                                   ______________________________________                                    

By using the etching conditions shown in the TABLE I, we can obtain, for example, favorable results shown in the following TABLE II.

                  TABLE II                                                         ______________________________________                                                      Etching method                                                                                      Magnetron                                                   Reactive Microwave discharge                                                   ion      plasma    type reactive                                Item           etching  etching   etching                                      ______________________________________                                         Etching rate    >0.5     >1        >1                                          (μm/min)                                                                    Selection ratio                                                                               >10      >10       >10                                              for silicon and                                                                silicon and photo-                                                             resist material                                                            Anisotropy      <1/100   <1/100    <1/100                                          ratio of length                                                                of side etching                                                                to etching depth                                                           ______________________________________                                    

The TABLE II shows the results obtained in a case where silicon is etched by using an SF₆ gas as an etching gas. In other cases, favorable results similar to those shown in the TABLE II were obtained by using the etching conditions shown in the TABLE I.

EMBODIMENT I

FIG. 1 shows experimental results obtained in a case where a substrate made of monocrystalline silicon was subjected to reactive ion etching using an SF₆ gas plasma, under conditions that input power was equal to 450 W, and a gas pressure was equal to 65 m Torr. In FIG. 1, a solid curve 1 indicates a relationship between the temperature of the silicon substrate and the etching rate for the silicon substrate in the direction of the depth therein, a solid curve 2 indicates a relationship between the temperature of the silicon substrate and the etching rate for a photoresist film for forming a mask pattern, and a broken curve 3 indicated a relationship between the temperature of the silicon substrate and the normalized side etching. The term "normalized side etching" means a ratio of the length of side etching measured from the edge of a mask pattern to the etching depth. When the temperature of the silicon substrate was made lower than -90° C. and a self-bias voltage of -100 V was applied to the silicon substrate, the etching rate for the photoresist film became less than one-half an etching rate for the photo-resist film at 20° C. and the normalized side etching became less than 10⁻². Further, it was confirmed that a bias voltage of -10 to -100 V was required for making the selection ratio (namely, a ratio of the etching rate for the silicon substrate to that for the photoresist film) greater than ten. Further, even when the temperature of the silicon substrate was made lower than -80° C., the etching rate for the silicon substrate in the direction depth therein was in the order of 5,000 Å/min, that is, was substantially equal to an etching rate at 20° C., and the silicon substrate was etched at high speed so long as the gas pressure was made higher than 60 m Torr. Thus, in the present embodiment, dry etching was carried out under conditions that the input power was 450 W, the temperature of the silicon substrate was made lower than -90° C., the gas pressure was made higher than 60 m Torr and the bias voltage applied to the silicon substrate was put in a range from -100 to -10 V, to obtain a high etching rate for the silicon substrate and a selection ratio of 10 or more, and to increase the degree of anisotropy in etching. The etching rate for the silicon substrate could be varied by changing the pressure of the SF₆ gas and the input power. Further, it was confirmed that when dry etching was carried out under conditions shown in the TABLE I, all of three requirements (that is, a high etching rate, high selectivity and marked anisotropy) were satisfied.

EMBODIMENT II

In the present embodiment, microwave plasma etching or magnetron discharge type reactive etching was carried out in accordance with the present invention.

An SF₆ gas was used as an etching gas, to etch a polysilicon film kept at various temperatures within a range from +20° C. to -140° C. by the microwave plasma etching method. FIGS. 2, 3 and 4 show a relationship between the pressure of the SF₆ gas and the etching rate for the polysilicon film, a relationship between the pressure of the SF₆ gas and the normalized side etching (namely, a ratio of the length of side etching to the etching depth), and a relationship between the pressure of the SF₆ gas and the selection ratio (namely, a ratio of the etching rate for the polysilicon film to that for a photoresist film), respectively. In the above etching process, a microwave power of 200 W was supplied to the SF₆ gas, and a vias voltage of -50 to -10 V was applied to the polysilicon film. As is apparent from FIGS. 2, 3 and 4, when the pressure of the SF₆ gas was made higher than 4 m Torr and the temperature of the polysilicon film was put in a range from -100° C. to -135° C., the etching rate was higher than 1 μm/min, the side etching was nearly equal to zero, and the selection ratio was greater than 10. Further, in a case where the above polysilicon film was etched by the magnetron discharge type reactive etching method, favorable results similar to the above-mentioned were obtained.

EMBODIMENT III

In the present embodiment, an NF₃ gas was used as an etching gas to etch a silicon substrate by the microwave plasma etching method or magnetron discharge type reactive etching method. When the temperature of the silicon substrate was made lower than -120° C., the pressure of the NF₃ gas was made higher than 1 m Torr, a bias voltage of -40 to -5 V was applied to the silicon substrate and an electric power of 250 W was supplied to the NF₃ gas, the etching rate for the silicon substrate became greater than 5,000 Å/min, a ratio of the etching rate for the silicon substrate to that for a photoresist mask became greater than ten, and the normalized side etching became less than 10⁻².

In a case where a PF₃ gas was used in place of the NF₃ gas, it was required to make the temperature of the silicon substrate lower than -90° C. Further, in a case where an F₂ gas was used in place of the NF₃ gas, high-accuracy etching was carried out by making the temperature of the silicon substrate lower than -90° C.

In all of the above cases, favorable results were obtained by using the etching conditions shown in the TABLE I.

EMBODIMENT IV

A Cl₂ gas was used as an etching gas to etch a silicon substrate ty the microwave plasma etching method or magnetron discharge type reactive etching method. In this case, when the temperature of the silicon substrate was made lower than -60° C., the pressure of the Cl₂ gas was made higher than 4 m Torr and a bias voltage of -20 to -100 V was applied to the silicon substrate, the etching rate for the silicon substrate became greater than 0.5 μm/min, a ratio of the etching rate for the silicon substrate to that for a photoresist film became greater than ten, and the normalized side etching became less than 10⁻². Further, a Cl₂ gas was used as an etching gas to etch a silicon substrate by the reactive ion etching method. In this case, when the pressure of the Cl₂ gas was made nearly equal to 100 m Torr, an electric power of 200 W was supplied to the Cl₂ gas, a bias voltage of -200 V was applied to the silicon substrate and the temperature of the silicon substrate was made lower than -50° C., favorable results were obtained. In a case where a Br₂ gas was used in place of the Cl₂ gas, high-accuracy etching was carried out by making the temperature of the silicon substrate lower than -40° C.

In the above, the Cl₂ or Br₂ gas was used as an etching gas. However, an etching operation excellent in working accuracy can be performed by using a mixture of a plurality of gases (for example, a mixture of SF₆ and Cl₂ or a mixture of NF₃ and Cl₂) as an etching gas. It was confirmed that the selection ratio was improved by changing the pressure and mixing ratio of a gas mixture used as an etching gas, with time.

EMBODIMENT V

FIG. 5 shows experimental results which were obtained in a case where an aluminum film kept at various temperatures within a range from -20° C. to 80° C. was etched by a reactive ion etching method using a Cl₂ gas as an etching gas, under conditions that the pressure of the Cl₂ gas was made equal to 200 m Torr, an electric power of 400 W was supplied to the Cl₂ gas and a bias voltage smaller than -200 V was applied to the aluminum film. In FIG. 5, a straight line 4 indicates a relationship between the temperature of the Al film and the etching rate for the Al film, a curve 5 indicates a relationship between the temperature of the Al film and the etching rate for a resist film formed on the Al film, and a curve 6 indicates a relationship between the temperature of the Al film and the normalized side etching. The etching of aluminum is accompanied with an exothermic reaction, and hence aluminum is heated to a temperature of 40 to 100° C. even when aluminum is etched while being cooled by cooling water. In the present embodiment, the etching rate for the Al film was 5,500 Å/min in a temperature range from -20° C. to +80° C., as indicated by the straight line 4 in FIG. 5. When the temperature of the Al film was made equal to -5° C., the etching rate for the resist film became less than one-half the etching rate for the resist film in a case where the Al film was cooled by cooling water, as indicated by the curve 5 in FIG. 5. Further, when the temperature of the Al film was made equal to -10° C., the normalized side etching was reduced to 10⁻². Thus, it was confirmed that when an Al film was etched by the reactive ion etching method using a Cl₂ gas under conditions that the temperature of the Al film was made lower than -10° C., the pressure of the Cl₂ gas was put in a range from 50 to 200 m Torr and a bias voltage smaller than -200 V was applied to the Al film, the working accuracy in etching was greatly improved.

In a case where a BCl₃ gas was used in place of the Cl₂ gas, the etching rate for the Al film was reduced by about 50%. However, owing to the boron deposition effect, the normalized side etching was reduced to 10⁻², even when the temperature of the Al film was kept at -5° C. That is, when the BCl₃ gas is used, high-accuracy etching can be carried out under an etching condition that the Al film is kept at -5° C.

EMBODIMENT VI

A film made of aluminum or an aluminum alloy was etched by the microwave plasma etching method and the magnetron discharge type reactive etching method each using a BCl₃ gas or Cl₂ gas as an etching gas, under conditions that the pressure of the etching gas was made higher than 2 m Torr, a bias voltage smaller than -50 V was used and the temperature of the film was made lower than -5° C. In this case, the etching rate was greater than 1 μm/min, the selection ratio (namely, a ratio of the etching rate for the Al or Al-alloy film to that for a resist film) was greater than ten, and the normalized side etching was less than 10⁻². The above etching rate for the Al or Al-alloy film was more than twice the etching rate in the reactive ion etching method. That is, it was known that when aluminum or an aluminum alloy was etched by a dry etching method, the microwave plasma etching method and the magnetron discharge type reactive etching method were superior to the reactive ion etching method.

EMBODIMENT VII

A tungsten film was etched while using a resist film as a mask by the microwave plasma etching method or magnetron discharge type reactive etching method under conditions that an SF₆ gas was used as an etching gas, the pressure of the SF₆ gas was made equal to 5 m Torr and a microwave power of 300 W was supplied to the SF₆ gas. In this case, when the temperature of the tungsten film was made lower than 0° C., favorable results were obtained. Further, the etching rate for the tungsten film increased as the radio-frequency power was larger, and favorable microwave plasma etching was carried out by putting the pressure of the SF₆ in a range from 5 to 20 m Torr and making the bias voltage smaller than -40 V. That is, when the tungsten film was etched by the microwave plasma etching method or magnetron discharge type reactive etching method under conditions that the pressure of the SF₆ gas was made higher than 5 m Torr, the radio-frequency power was so increased as to make the bias voltage smaller than -40V, and the temperature of the tungsten film was made lower than 0° C., the etching rate for the tungsten film became higher than 1 μm/min, the selection ratio became greater than ten, and the normalized side etching was reduced by a great degree.

EMBODIMENT VIII

When fluorocarbon gases such as C₃ F₈, C₂ F₆, and CHF₃ are used as an etching gas to etch SiO₂ and Si₃ N₄, these gases do not produce a deposit on SiO₂ and Si₃ N₄ However, when these gases are used to etch silicon and tungsten, a deposit is produced on silicon and tungsten. In more detail, when the fluorocarbon gases are used to etch SiO₂, SiO₂ reacts with CF₂, and reaction products SiF₄ and CO (or CO₂) evaporate. Accordingly, a deposit containing carbon or a monomer CF_(n) is not produced.

An SiO₂ film was etched by the microwave plasma etching method using a CHF₃ gas as an etching gas, under conditions that the pressure of the CHF₃ gas was made equal to 2 m Torr and an electric power of 400 W was supplied to the CHF₃ gas. In this case, the etching rate for the SiO₂ film was 5,000 μ/min. In order to make the normalized side etching less than 10⁻² and make a ratio of the etching rate for the SiO₂ film to that for a resist film greater than 15, while keeping an etching rate of 5,000 Å/min, it was necessary to make the temperature of the SiO₂ lower than -60° C. In the above etching process, a bias voltage of -100 V was applied to the SiO₂ film. In a case where a bias voltage smaller than -100 V was used, the etching rate for the SiO₂ film was reduced, and it was necessary to put the temperature of the SiO₂ film in a range from -50° C. to -40° C. In a case where one of fluorocarbon gases such as C₂ F₆ and C₃ F₈ or a gas mixture of one of the fluorocarbon gases and helium was used as an etching gas to etch an SiO₂ film by the microwave plasma etching method, when the pressure of the etching gas was made higher than 2 m Torr, a bias voltage smaller than -100 V was applied to the SiO₂ film and the temperature of the SiO₂ film was made lower than -40° C., both a high etching rate and a high selective ratio were obtained, and moreover the normalized side etching was reduced to a very small value.

When an Si₃ N₄ film was etched by the microwave plasma etching method using one of the fluorocarbon gases CHF₃, C₂ F₆ and C₃ F₈ or a gas mixture CF₄ +O₂ as an etching gas under conditions that the pressure of the etching gas was made higher than 2 m Torr, a bias voltage smaller than -100 V was applied to the Si₃ N₄ film and the temperature of the Si₃ N₄ film was made lower than -40° C., favorable results were obtained.

EMBODIMENT IX

An etching gas suitable for etching a silicide film made of one of WSi₂, CoSi₂, TaSi₂ and others, and a temperature of the silicide film were studied, and it was confirmed that the etching gas for and the temperature range of the silicide film were substantially the same as an etching gas for and a temperature range of a monocrystalline or polycrystalline silicon film. In more detail, when an SF₆ gas was used as an etching gas, it was required to make the temperature of the silicide film lower than -90° C. When a Cl₂ gas was used as an etching gas, it was required to make the temperature of the silicide film lower than -60° C. Similarly to a case where the monocrystalline or polycrystalline silicon film was etched, the pressure of the etching gas was required to be higher than 5 m Torr. Further, it was favorable to apply a self-bias voltage smaller than -50 V to the silicide film.

EMBODIMENT X

A gas containing chloride was used as an etching gas to etch GaAs under conditions that the pressure of the etching gas was made higher than 2 m Torr, a bias voltage smaller than -50 V was applied to the article to be etched and the temperature thereof was made lower than 0° C. In this case, favorable results were obtained.

It was possible to etch InP in a manner similar to the above-mentioned. In this case, however, it was necessary to keep the article to be etched at a temperature of 2 to 3° C.

Ternary compound semiconductors such as AlGaAs and InGaP were etched in substantially the same manner as mentioned above, and favorable results were obtained.

Further, superconductive materials such as Nb, Pb and Zr were etched in a similar manner. When an article to be etched was kept at a temperature lower than 5° C., the material was etched with a high accuracy.

The above-mentioned temperature ranges held in all of a parallel plate type reactive ion etching apparatus, a microwave plasma etching apparatus, a magnetron discharge type reactive etching apparatus, and other dry etching apparatuses using a plasma or an ion. Further, by selecting the gas pressure, the temperature of the article to be etched and the self-bias voltage applied thereto, appropriately in each of the above etching apparatuses, it was possible to make the etching rate for the article to be etched greater than 1 μm/min and to make the selection ratio greater than ten.

As is evident from the foregoing explanation, according to the present invention, various materials can be dry-etched with a high etching rate, a high selective ratio and marked anisotropy. That is, a dry etching method according to the present invention can reduce the number of manufacturing steps and the frequency of fault. 

We claim:
 1. A dry etching method comprising the steps of:disposing an article to be etched in the reaction chamber of an etching apparatus, a mask made of a photoresist film having a predetermined pattern being formed on a surface of the article to be etched, wherein said surface of said article to be etched is made of a material selected from the group consisting of Si, Al, W, SiO₂, Si₃ N₄ and a silicide; and putting the article to be etched in contact with the plasma of an etching gas while controlling the pressure of said etching gas, applying a bias voltage in a range from -10 to -100 V and controlling the temperature of the article to be etched at lower than 0° C. so as to etch the surface of the article to be etched in a condition that the gas pressure in the reaction chamber, the bias voltage applied to the article to be etched and the temperature of the article to be etched are set as to make it possible to make the etching rate for the article to be etched higher than 0.5 μm/min, to make a ratio of the etching rate for the article to be etched to the etching rate for the mask greater than ten, and to make a ratio of the length of side etching in the article to be etched to the depth of etching in the article to be etched less than 1/100.
 2. A dry etching method according to claim 1, wherein the etching apparatus is one of a microwave plasma etching apparatus and a magnetron discharge type reactive etching apparatus, and wherein the gas pressure is put in a range from 4 to 10 m Torr, the bias voltage is put in a range from -10 to -50 V, and the temperature of the article to be etched is put in a range from -100 to -135° C.
 3. A dry etching method according to claim 2, wherein said etching gas is free of carbon and silicon.
 4. A dry etching method according to claim 3, wherein said etching gas contains at least one gas selected from the group consisting of SF₆, NF₃, PF₃, F₂, Cl₂, Br₂ and BCl₃.
 5. A dry etching method according to claim 1, wherein said etching gas is free of carbon and silicon.
 6. A dry etching method according to claim 5, wherein said etching gas contains at least one gas selected from the group consisting of SF₆, NF₃, PF₃, F₂, Cl₂, Br₂ and BCl₃.
 7. A dry etching method comprising the steps of:disposing an article to be etched in the reaction chamber of an etching apparatus, a mask made of a photoresist film having a predetermined pattern being formed on a surface of the article to be etched; and putting the article to be etched in contact with the plasma of an etching gas while controlling the pressure of said etching gas, applying a bias voltage in a range from -10 to -100 V and controlling the temperature of the article to be etched to etch the surface of the article to be etched in a condition that the gas pressure in the reaction chamber, the bias voltage applied to the article to be etched and the temperature of the article to be etched are set as to make it possible to make the etching rate for the article to be etched higher than 0.5 μm/min, to make a ratio of the etching rate for the article to be etched to the etching rate for the mask greater than ten, and to make a ratio of the length of side etching in the article to be etched to the depth of etching in the article to be etched less than 1/100, wherein the etching apparatus is a reactive ion etching apparatus, and wherein the gas pressure is put in a range from 60 to 100 m Torr, the bias voltage is put in a range from -30 to -100 V, and the temperature of the article to be etched is put in a range from -90 to -135° C.
 8. A dry etching method according to claim 7, wherein the power density supplied to the reactive ion etching apparatus lies in a range from 0.2 to 0.4 W/cm².
 9. A dry etching method according to claim 7, wherein said etching gas is free of carbon and silicon.
 10. A dry etching method according to claim 9, wherein said etching gas contains at least one gas selected from the group consisting of SF₆, Cl₂, and BCl₃.
 11. A dry etching method comprising the steps of:disposing an article to be etched in the reaction chamber of an etching apparatus, a mask made of a photoresist film having a predetermined pattern being formed on a surface of the article to be etched; and putting the article to be etched in contact with the plasma of an etching gas while controlling the pressure of said etching gas, applying a bias voltage in a range from -10 to -100 V and controlling the temperature of the article to be etched to etch the surface of the article to be etched in a condition that the gas pressure in the reaction chamber, the bias voltage applied to the article to be etched and the temperature of the article to be etched are set as to make it possible to make the etching rate for the article to be etched higher than 0.5 μm/min, to make a ratio of the etching rate for the article to be etched to the etching rate for the mask greater than ten, and to make a ratio of the length of side etching in the article to be etched to the depth of etching in the article to be etched less than 1/100, wherein the etching apparatus is the microwave plasma etching apparatus, and an electric power of 200 to 400 W is supplied to the mcirowave plasma etching apparatus and wherein the gas pressure is put in a range from 4 to 10 m Torr, the bias voltage is put in a range from -10 to -50 V, and the temperature of the article to be etched is put in a range from -100° to -135° C.
 12. A dry etching method according to claim 11, wherein said etching gas is free of materials which can deposit a film on the article to be etched.
 13. A dry etching method according to claim 12, wherein the article to be etched is a film made of a material selected from the group consisting of SiO₂ and Si₃ N₄ and wherein said etching gas contains a fluorocarbon gas.
 14. A dry etching method according to claim 13, wherein said article to be etched comprises a film of SiO₂ and said fluorocarbon gas is at least one of C₃ F₈, C₂ F₆ and CHF₃.
 15. A dry etching method according to claim 13, wherein said article to be etched comprises a film of Si₃ N₄ and said fluorocarbon gas is at least one gas selected from the group consisting of C₃ F₈, C₂ F₆ and CHF₃ or a gas mixture of CF₄ and O₂.
 16. A dry etching method, comprising the steps of:disposing an article to be etched in the reaction chamber of an etching apparatus, a mask made of a photoresist film having a predetermined pattern being formed on a surface of the article to be etched; and putting the article to be etched in contact with the plasma of an etching gas while controlling the pressure of said etching gas, applying a bias voltage in a range from -10 to -100V and controlling the temperature of the article to be etched at lower than 0° C. so as to etch the surface of the article to be etched in a condition that the gas pressure in the reaction chamber, the bias voltage applied to the article to be etched and the temperature of the article to be etched are set as to make it possible to make the etching rate for the article to be etched higher than 0.5 μm/min, to make a ratio of the etching rate for the article to be etched to the etching rate for the mask greater than ten, and to make a ratio of the length of side etching in the article to be etched to the depth of etching in the article to be etched less than 1/100; wherein the etching apparatus is a magnetron discharge type reactive etching apparatus, and an electric power of 0.2 to 0.4 W is supplied to the magnetron discharge type reactive etching apparatus and wherein the gas pressure is put in a range from 4 to 10 m Torr, the bias voltage is put in a range from -10 to -50 V, and the temperature of the article to be etching is put in a range from -100 to -135° C. 